Lincoln Electric, ED037282, Metal-Cored Wire, 0.052 in; 1.3 mm, 750 lb Accu-Trak Drum, E70C-6M-H4; E70T15-M21A4-CS1-H4

Metalshield® MC-70 XLS™ from Lincoln Electric is a mild steel metal-cored wire designed with minimal silicon islands for an exceptionally clean weld surface and minimal post weld clean up.

What's Included?

• (1) 750 lb Accu-Trak® Drum

• Consumables Material: Metal-Cored Gas-Shielded (GMAW-C)
• Consumable Diameter: 0.052 in (1.3 mm)
• Weight: 750 lb
• Classification: E70C-6M-H4; E70T15-M21A4-CS1-H4
• Alloy Type: SM
• Winding: NOS
• Welding Process: MCAW
• Country of Origin: Canada
• AWS Specification: E70C-6M-H4, E70T15-M21A4-CS1-H4
• Compliance: AWS A5.18, ASME SFA-A5.18, AWS A5.36, ASME SFA-A5.36, CWB/CSA W48-06
• Shielding Gas: 75-92% Argon / Balance CO2, Flow rate 40-60 CFH
• Yield Strength: 400 MPa (58 ksi) min
• Tensile Strength: 480 MPa (70 ksi) min
• Elongation: 22% min
• Charpy V-Notch Impact: 27 J (20 ft lbf) min @ -40 C (-40 F)
• Typical Tensile Strength Range: 490-660 MPa (70-95 ksi)
• Typical Yield Strength Range: 450-550 MPa (65-80 ksi)
• Typical Elongation Range: 26-30%
• Typical Charpy V-Notch Impact Range: 40-105 J (30-75 ft lbf) @ -40 C (-40 F)
• Deposit Composition - Carbon (C): 0.04-0.07%
• Deposit Composition - Manganese (Mn): 1.25-1.60%
• Deposit Composition - Silicon (Si): 0.55-0.85%
• Deposit Composition - Sulfur (S): 0.010-0.020%
• Deposit Composition - Phosphorus (P): 0.005-0.010%
• Deposit Composition - Copper (Cu): 0.01-0.05%
• Deposit Composition - Nickel (Ni): 0.30-0.40%
• Deposit Composition - Chromium (Cr): 0.01-0.03%
• Deposit Composition - Molybdenum (Mo): 0.01-0.02%
• Deposit Composition - Vanadium (V): 0.01-0.02%
• Diffusible Hydrogen: 2-4 mL/100g weld deposit
• Welding Positions: Flat & Horizontal (CV processes), Out of Position (Pulse waveforms)