Harris Products Group, 955A318SP, Solder Wire, 95/5 Lead-Free, Acid Core, Elevated Temperature Applications, Complies with EU Reach & RoHS

95/5 acid core tin-antimony solder is a lead-free alloy frequently used to solder copper, brass, and steel, often as a replacement for lead bearing alloys. Flux is contained in the solder core and flows out to protect the surface during heating. This solder form minimizes the amount of flux used per part and makes it an ideal choice for semi-automated soldering applications. 95/5 has a higher melting temperature vs. tin/lead solders which is helpful in certain elevated temperature service applications. 95/5 has a narrow melting range providing rapid flow when melted. This trait means parts with reasonably close tolerances (0.002 in. – 0.005 in.) are recommended. Wire is manufactured per composition ASTM B32 Alloy Sb-5. Complies with the EU Reach & RoHS directive.

Features

• Silver/gray color as deposited
• Higher melting temperature than tin-lead solders
• Ideal for elevated temperature service applications
• Meets ASTM B32 - Sb5 (solder wire component);STD-006, Sn95Sb5A Flux core - J STD - 004 type ORM1
• Acid core flux tin-antimony solder
• Used to solder copper, brass and steel and semi-automated soldering applications
• No additional flux is necessary
• Narrow melting range yields rapid flow when melted
• Complies with the EU Reach & RoHS directive

• Shear Strength at Room Temperature: 5613 PSI
• Shear Strength at 212 F: 3089 PSI
• Melting Point Range: 455 F - 464 F (235 C - 240 C)
• Electrical Resistivity: 0.145 m
• Weight: 1 lbs
• Recommended Tolerance: 0.002 in 0.005 in
• Density: 7.26 g/cm3
• Composition: 95% Tin, 5% Antimony
• Flux Core Type: Acid Core
• Specification Compliance: ASTM B32 Sb5, J-STD-006 Sn95Sb05A, J-STD-004 Type OR
• Environmental Compliance: EU Reach, RoHS
• Color: Silver/Gray