Harris Products Group, 308LT505POP, TIG Welding Alloy, 308L, 87,000 psi tensile strength, 0.03% carbon content, ANSI/AWS A5.9

308L stainless steel TIG (GTAW) welding alloy is most frequently used for welding base metals of similar composition. The 0.03% maximum carbon content increases its resistance to intergranular corrosion. Conforms to AWS A5.9.

Features

• 87,000 psi tensile strength (as welded)
• 56% reduction of area (as welded)
• Stainless steel 308L TIG welding rod welds base metals of similar composition
• 85 HRB Rockwell B hardness (as welded)
• 57,000 psi yield strength (as welded)
• 100 ft./lb. @ room temperature Charpy V (as welded)
• 34% elongation (as welded)
• 160 HB Brinell hardness (as welded)
• Lower carbon content (0.03% maximum) resists carbide precipitation that can cause weld corrosion
• Conforms to ANSI/AWS A5.9 & ASME SFA 5.9 ER 308L

• Tensile Strength: 87,000 psi
• Yield Strength: 57,000 psi
• Charpy V Impact: 100 ft-lb @ room temperature
• Hardness: 85 HRB Rockwell B, 160 HB Brinell
• Reduction of Area: 56%
• Elongation: 34%
• Carbon Content: 0.03% max
• Weight: 1.03 lbs
• Material: Stainless Steel 308L
• Compliance: ANSI/AWS A5.9, ASME SFA 5.9 ER 308L