Harris Products Group, 00015600POP, Brazing Rod, 1/8 in; 36 in, 1 lb, Aluminum Alloy, 1670 F-1750 F

Harris® 15 low fuming bronze is considered a “braze-welding” filler metal as this copper/zinc filler metal exhibits minimal capillary action during brazing. This limits joint design primarily to lap, tee, and butt joints. Butt joints require some edge preparation typically incorporating beveled edges to provide a location for filler metal to be applied and to ensure filler metal penetration to the joint root. LFB was developed primarily to braze steel and some cast iron grades including malleable and grey iron. It can be used to join copper but due to its elevated melting temperature care must be taken during brazing to avoid overheating or melting the copper. It is used with the oxy-fuel process. These filler metals are bare. Conforms to the EU Reach & RoHS directive. Conveniently packaged for point-of-purchase display.

Features

• 1670◦F to 1750◦F brazing temperature range
• Good machinability
• Color matches yellow brass
• Bare low-fuming bronze brazing alloy
• 65,000 psi tensile strength
• Conforms to the EU RoHS directive.
• Porosity - free deposits

Applications

• Brazing steel, some cast iron grades, copper, steel brackets, straps, angles and related fittings

• Tensile Strength: Up to 65,000 psi
• Brazing Temperature Range: 1670 F-1750 F (910 C-954 C)
• Diameter: 1/8 in (3.18 mm)
• Length: 36 in (914.4 mm)
• Weight: 1 lb
• Material: Aluminum alloy
• Solidus: 1590 F (866 C)
• Liquidus: 1630 F (888 C)
• Chemical Composition: Tin 0.80-1.10%; Copper 56-60%; Iron 0.25-1.20%; Manganese 0.01-0.50%; Silicon 0.04-0.15%; Zinc remainder; Lead 0.05% max; Aluminum 0.01% max; Others 0.50% max
• Compliance: RoHS Compliant
• Country of Origin: US
• Color: Yellow brass
• Classification: AWS A5.8 RBCuZn-C; ASME SFA 5.8 RBCuZn-C; ISO 17672 Cu681
• Warranty: 1 Year
• Made in USA: Yes