Harris Products Group, 0308L12, MIG Welding Wire, Stainless Steel 308L, 57,000 psi Yield Strength, 87,000 psi Tensile Strength, 0.03% Max Carbon Content

308L stainless steel MIG (GMAW) welding wire has similar usage as 308, but the 0.03% maximum carbon content increases resistance to intergranular corrosion. Most frequently used for welding base metals of similar composition. Conforms to AWS A5.9.

Features

• Stainless steel 308L MIG welding wire welds base metals of similar composition
• 57,000 psi yield strength (as welded)
• 85 HRB Rockwell B hardness (as welded)
• Conforms to ANSI/AWS A5.9 & ASME SFA 5.9 ER 308L
• Lower carbon content (0.03% maximum) resists carbide precipitation that can cause weld corrosion
• 34% elongation (as welded)
• 100 ft./lb. @ room temperature Charpy V (as welded)
• 56% reduction of area (as welded)
• 87,000 psi tensile strength (as welded)
• 160 HB Brinell hardness (as welded)

• Material: 308L Stainless Steel
• Yield Strength: 57,000 psi
• Tensile Strength: 87,000 psi
• Elongation: 34%
• Reduction of Area: 56%
• Charpy V Impact: 100 ft-lb @ room temperature
• Brinell Hardness: 160 HB
• Rockwell Hardness: 85 HRB
• Carbon Content: 0.03% max
• Compliance: ANSI/AWS A5.9, ASME SFA 5.9 ER 308L
• Weight: 1.1 lbs