Stoody, 11233600, Flux-Cored Welding Wire, 1/16 in; 170-225 Amps, Stainless Steel, SOS 309L

Stoodys "SOS" wires offer the productivity and efficiencies of continuous welding wire and the convenience and low cost of open arc (gas-less) welding. Welding can be done indoors or outdoors - even in moderate wind or draft conditions. Weldability is excellent, producing weld deposits that are sound and clean with flat to slightly convex bead shape.

Features

• Stoody® "SOS" wire deposits have lower percentage of penetration than GMAW deposits at the same current levels which means less dilution and distortion.
• Stoody®s "SOS" wires do not require specialized equipment.
• For best results, a content voltage, direct current power source is recommended.
• Stoody® "SOS" wires can be used as a direct replacement for solid stainless wires or electrodes of the same grade both in fabricating and overlay applications.

Prop 65

• Yes

• Amperage Range: 170 Amps - 225 Amps
• Diameter: 1/16 in.
• Material: Stainless Steel
• Process: FCAW
• Country of Origin: United States
• Trade Name: SOS 309L
• Carcinogen: Carbon Black
• Reproductive: Dual Short Form
• AWS/SFA Classification: A5.22: 2010 E309LT0-3
• Tensile Strength: 88 Ksi (610 MPa)
• Elongation: 38%
• Carbon Content: 0.02%
• Manganese Content: 1.2%
• Silicon Content: 0.5%
• Chromium Content: 24.4%
• Nickel Content: 12.6%
• Ferrite Number: 15.0
• Welding Current Type: Direct Current Electrode Positive (DCEP)
• Recommended Power Source: Constant voltage, direct current
• Optimal Welding Voltage Range: 26-28 V
• Wire Feed Speed Range: 175-290 in/min (4.5-7.4 m/min)
• Wire Extension: 5/8 in to 3/4 in (13-19 mm)