Stoody, 11231200, Flux-Cored Welding Wire, SOS 309L, 3/32 in, Stainless Steel, 275-320 A

Stoodys "SOS" wires offer the productivity and efficiencies of continuous welding wire and the convenience and low cost of open arc (gas-less) welding. Welding can be done indoors or outdoors - even in moderate wind or draft conditions. Weldability is excellent, producing weld deposits that are sound and clean with flat to slightly convex bead shape.

Features

• For best results, a content voltage, direct current power source is recommended.
• Stoody® "SOS" wires can be used as a direct replacement for solid stainless wires or electrodes of the same grade both in fabricating and overlay applications.
• Stoody®s "SOS" wires do not require specialized equipment.
• Stoody® "SOS" wire deposits have lower percentage of penetration than GMAW deposits at the same current levels which means less dilution and distortion.

Prop 65

• Yes

• Amperage: 275-320 A
• Diameter: 3/32 in
• Material: Stainless Steel
• Process: FCAW
• Voltage: 28-30 V
• Wire Feed Speed: 175-250 in/min (4.5-6.4 m/min)
• Wire Extension: 1 1/4 to 3/4 in (32 to 19 mm)
• Welding Current Polarity: DCEP (Direct Current Electrode Positive)
• Tensile Strength: 88 Ksi (610 MPa)
• Elongation: 38 %
• Carbon Content: 0.02 wt%
• Manganese Content: 1.2 wt%
• Silicon Content: 0.5 wt%
• Chromium Content: 24.4 wt%
• Nickel Content: 12.6 wt%
• Ferrite Number: 15.0
• AWS/SFA Classification: A5.22: 2010 E309LT0-3