Lincoln Electric, ED034413, Flux-Cored Wire, E81T1-Ni1M-JH4; 1/16 in; 33 lb Spool

Designed for high strength, low-alloy applications using 75% Argon/25% CO2. The use of mixed shielding gas stabilizes arc characteristics, reduces spatter levels, and washes out the weld bead for a flat appearance.

What's Included?

• (1) 33 lb Spool

Features

• ProTech® foil bag packaging
• Designed for welding with 75-85% Argon/Balance CO2 shielding gas
• Meets AWS D1.8 seismic lot waiver requirements
• Capable of producing weld deposits with impact toughness exceeding 88 - 123 J (65 - 91 ft·lbf) at -40°C (-40°F)
• Notes: AWS D1.8 structural steel seismic supplement test data can be found at the Lincoln Electric Certificate Center.
• Premium arc performance and bead appearance

• Welding Process: FCAW-G
• Classification: E81T1-M21A4-Ni1-H4, E81T1-Ni1M-JH4
• Diameter: 1/16 in (1.6 mm)
• Spool Weight: 33 lb
• Material: Flux-cored (FCAW-G) Wire, Low Alloy (SLA)
• Alloy Type: SLA
• Shielding Gas: 75-85% Argon, Balance CO2
• Impact Toughness: 88-123 J (65-91 ft lbf) at -40 C (-40 F)
• Yield Strength: 470 MPa (68 ksi) min
• Tensile Strength: 550-690 MPa (80-100 ksi)
• Elongation: 19% min
• Charpy V-Notch Impact Energy: 27 J (20 ft lbf) min at -29 C (-20 F) and -40 C (-40 F)
• Typical Deposit Composition - Carbon (C): 0.04-0.05%
• Typical Deposit Composition - Manganese (Mn): 1.26-1.36%
• Typical Deposit Composition - Silicon (Si): 0.25-0.29%
• Typical Deposit Composition - Sulfur (S): 0.006-0.009%
• Typical Deposit Composition - Phosphorus (P): 0.005-0.008%
• Typical Deposit Composition - Nickel (Ni): 0.86-0.96%
• Typical Deposit Composition - Molybdenum (Mo): 0.01%
• Typical Deposit Composition - Chromium (Cr): 0.04-0.05%
• Typical Deposit Composition - Vanadium (V): 0.02-0.03%
• Diffusible Hydrogen: 2-4 mL/100g weld deposit max
• Country of Origin: United States