Harris Products Group, 0H336R, Brazing Alloy, Phos-Copper, Self-Fluxing, 1.02 lb

Harris® 0HP phos-copper brazing alloy is an economical brazing filler metal (very fluid medium temperature brazing alloy) for joining copper, brass, and bronze. Will withstand moderate vibration. Recommended joint clearance is .002 in. - .005 in. Stay Silv 0HP, (and other phosphorus containing filler metals), should not be used to braze ferrous or nickel alloy base metals. Complies with the EU Reach & RoHS directive.

Features

• Recommended joint clearance of 0.002 in. - 0.005 in. (0.05 mm - 0.13 mm)
• Copper is self-fluxing, so no manual flux application is required
• Primarily used in manual brazing applications
• Suitable for brazing brass
• Corrosion resistance is generally similar to the copper base metal, but phosphorus containing alloys, including Harris® 0HP, should not be used if the braze is exposed to sulfur or sulfur compounds in service
• Alloy flows quickly at brazing temperature requiring close joint tolerance, less than 0.005 in. (0.13 mm)
• When brazing brass, operators should avoid over heating and use Stay Silv® white brazing flux
• Not recommended for brazing steel or other ferrous base metals
• Complies with the EU Reach & RoHS directive
• Economical choice for copper brazing

• Weight: 1.02 lbs
• Chemical Composition - Phosphorus: 7.0-7.4%
• Chemical Composition - Copper: Remainder
• Chemical Composition - Others: 0.15% max
• Solidus Temperature: 1310 F (710 C)
• Liquidus Temperature: 1450 F (788 C)
• Specific Gravity: 8.21
• Recommended Joint Clearance: 0.002 in - 0.005 in (0.05 mm - 0.13 mm)
• Material Type: Phosphorus Copper Alloy
• Suitable For: Copper, Brass, Bronze
• Not Suitable For: Ferrous or Nickel Alloy Base Metals
• Flux Requirement: No flux required for copper brazing; white flux recommended for brass
• Corrosion Resistance: Similar to copper base metal; avoid sulfur exposure
• Compliance: EU Reach, RoHS
• Vibration Resistance: Withstands moderate vibration