Harris Products Group, 0320R1, Brazing Rod, 1/16 in; Phos-Copper Alloy, 20 in, Fluidity Rating 5

Harris® 0 phos-copper brazing filler metal is a low cost filler metal use for many copper-to-copper applications where moderate fit-up can be maintained and brazing temperature is not critical. Conforms to the EU Reach & RoHS directive. Conforms to the EU Reach & RoHS directive.

Notes

• The higher the fluidity rating, the faster the alloy flows within the melting range

Features

• Corrosion resistance is generally similar to copper base metal, but phosphorus containing alloys should not be used if the braze is exposed to sulfur or sulfur compounds in service
• An economical choice for copper brazing
• Due to its phosphorus content should not be used if the braze is exposed to sulfur or sulfur compounds in service.
• Alloy flows quickly at brazing temperature so requires close joint tolerance (less than 0.005")
• Copper is self-fluxing
• Operators should avoid over heating the brass and use Stay Silv® white brazing flux
• Also a suitable for brazing brass
• Primarily used in manual brazing applications
• Not recommended for brazing steel or other ferrous base metals

Applications

• Brazing copper-to-copper, copper-to-brass, brass joints

• Fluidity Rating: 5
• Diameter: 1/16 in (1.59 mm)
• Length: 20 in (508 mm)
• Material: Phos-copper alloy
• Liquidus Temperature: 1460 F (793 C)
• Solidus Temperature: 1310 F (710 C)
• Brazing Temperature Range: 1345 F-1500 F (730 C-816 C)
• Recommended Joint Clearance: .002"-.007" (.051mm-.178mm)
• Warranty: 1 Year
• Electrical Resistivity: 19.2 Microhm/cm
• Electrical Conductivity: 9.9 %IACS
• RoHS Compliance: Yes
• NSF Compliance: No
• Country of Origin: US
• Compliance: EU Reach, RoHS
• Classification: AWS A5.8 BCuP-2; ASME Section IIC SFA 5.8 BCuP-2; ISO 17672 CuP 181