Harris Products Group, 015FC500POP, Brazing Rod, Aluminum Alloy, 3/32 in Diameter, 36 in Length, 1 lb, 1670 F to 1750 F Brazing Temp, Up to 65,000 psi Tensile Strength

Harris® 15 low fuming bronze is considered a “braze-welding” filler metal as this copper/zinc filler metal exhibits minimal capillary action during brazing. This limits joint design primarily to lap, tee, and butt joints. Butt joints require some edge preparation typically incorporating beveled edges to provide a location for filler metal to be applied and to ensure filler metal penetration to the joint root. LFB was developed primarily to braze steel and some cast iron grades including malleable and grey iron. It can be used to join copper but due to its elevated melting temperature care must be taken during brazing to avoid overheating or melting the copper. It is used with the oxy-fuel process. These filler metals are flux-coated. Conforms to the EU Reach & RoHS directive. Conveniently packaged for point-of-purchase display.

Applications

• Brazing steel, some cast iron grades, copper, steel brackets, straps, angles and related fittings

Features

• Porosity - free deposits
• Good machinability
• Flux coating provides excellent wetting action with no objectable fuming
• 1670◦F to 1750◦F brazing temperature range
• Color matches yellow brass
• 65,000 psi tensile strength
• Flux-coated low-fuming bronze brazing alloy

• Brazing Temperature Range: 1670 F-1750 F (910 C-954 C)
• Tensile Strength: Up to 65,000 psi
• Length: 36 in. (914.4 mm)
• Diameter: 3/32 in. (2.38 mm)
• Weight: 1 lb.
• Material: Aluminum alloy
• Color: Yellow brass
• Country of Origin: US
• Made in USA: Yes
• Classification: AWS A5.8 RBCuZn-C; ASME SFA 5.8 RBCuZn-C; ISO 17672 Cu681
• Recommended Flux: No flux required
• Chemical Composition: Tin 0.80-1.10%; Copper 56-60%; Iron 0.25-1.20%; Manganese 0.01-0.50%; Silicon 0.04-0.15%; Zinc Remainder%; Lead 0.05% max.; Aluminum 0.01% max.; Others (Total) 0.50% max.
• Liquidus: 1630 F (888 C)
• Solidus: 1590 F (866 C)
• Warranty: 1 Year
• NSF Compliant: No
• RoHS Compliant: No