Harris Products Group, 00015A0, Brazing Alloy, Copper-Zinc, Limited Joint Designs, Oxy-Fuel Process

Harris® 15 low fuming bronze (LFB) bare is considered a “braze-weld” alloy as this copper/zinc alloy exhibits minimal capillary action during brazing. This limits joint design primarily to lap, tee, and butt joints. Butt joints require some edge preparation typically incorporating beveled edges to provide a location for filler metal to be applied and to ensure alloy penetration to the joint root. LFB was developed primarily to braze steel and some cast iron grades including malleable and gray iron. It can be used to join copper but due to its elevated melting temperature care must be taken during brazing to avoid overheating or melting the copper. It is used with the oxy-fuel process.

Features

• Good color match to brass
• Exhibits minimal capillary action during brazing
• Copper-zinc braze-weld bare rod using oxy-fuel
• Good machinability
• Developed to braze steel and some cast iron grades, including malleable and gray iron. Also, joins copper
• Produces porosity-free deposits
• Corrosion resistance is similar to most high zinc brass alloys. Care should be taken on service conditions where water immersion is involved as dezincification is a potential issue.
• Limited joint designs to lap, tee and butt joints, although butt joints require some edge preparation

• Weight: 1.01 lbs
• Material: Copper, Zinc
• Tin Content: 0.80 1.10%
• Copper Content: 56.0 60.0%
• Iron Content: 0.25 1.20%
• Manganese Content: 0.01 0.50%
• Silicon Content: 0.04 0.15%
• Zinc Content: Remainder
• Lead Content: 0.05% max
• Aluminum Content: 0.01% max
• Other Elements: 0.50% max
• Solidus Temperature: 1590 F (866 C)
• Liquidus Temperature: 1630 F (888 C)
• Brazing Range: 1670 F 1750 F (910 C 955 C)
• Application Process: Oxy-fuel brazing
• Joint Types: Lap, Tee, Butt
• Compliance: AWS A5.8 RBCuZn-C, ASME SFA 5.8 RBCuZn-C, ISO 17672 Cu681